| Product Description |
2-part PUR adhesive
SP21X ( SP211, SP212, SP213, SP214)
This high-strength 2-part adhesive in the practical twin cartridge with static mixing tube achieves constructional force-locked connections with an excellent heat and weather resistance. Because of its wide adhesion spectrum, this adhesive can be used for a lot of different application fields, e.g. for Aluminium window and door manufacturing for bonding of corner connectors, in the dry construction for the friction-locked joint bonding of gypsum fibre boards and granulate cement plates and can be applied for joints
SP211- Two part PU structural adhesive, 15 mins of curing time, suitable for most areas
SP212- Two part PU structural adhesive, 25 mins of curing time, suitable for most areas
SP213- Two part PU structural adhesive, 30 mins of curing time, suitable for hot areas
SP214- Two part PU structural adhesive, 8-10 mins of curing time, suitable for cold areas
SP118- One part PU structural adhesive for general purpose
SPECIAL CHARACTERISTICS
APPLICATION EXAMPLES
| Specification Data Sheet |
| Item | Standard | Values | ||||
| Product name | --visual | SP215 | SP212 | SP213 | SP214 | |
| Appearance (visual ) | -- | White, smooth paste without particles | ||||
| Density g/cm³ | -- | 1.5±0.1 | ||||
| Sagging (mm) | ≤3 | 0-2 | ||||
| Mixing ratio V:V | -- | 100:100 | ||||
| Application time (min) | ≥10 | 15 | 25 | 40 | 5 | |
| Tack free time min | -- | 30±5 | 30±5 | 50±5 | 5 | |
| Bending test (bending deformation) (mm) |
≥4 | >15 (At break) |
>18 (No crack) |
|||
Hardness (Shore D) |
1H | -- | 2 | 0 | 0 | 58 |
| 2H | -- | 16 | 32 | 0 | 70 | |
| 3H | -- | 32 | 48 | 10 | 72 | |
| 4H | -- | 50 | 55 | 32 | 80 | |
| 5H | -- | 54 | 62 | 40 | 84 | |
| 24H | ≥60 | >70 | ||||
| 7 days | >75 | |||||
| Shear strength (MPa) (Alu/Alu) |
24H | ≥2 | ≥4 | |||
| 7 days | ≥3 | ≥6 | ||||
| Temperature resistance(%) | -- | -50~+100 ºC | ||||
| Application temperature ºC | -- | 5~+40 ºC | ||||
| Shelf life(month) | -- | 6 months and 9 months | ||||
| Note:All data above were tested under special condition (7 days after full cured). Testing standard:JC/T 25620-2002 |
||||||